Boda BDT601P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zdgxKN_Boda-BDT601P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDT601P is a high viscosity curative incorporated fluoroelastomer terpolymer. This grade is well suited for application where good compression set resistance and superior fluid resistance than copolymers are required. BDT601P can be compounded to meet the major fluoroelastomer specifications. BDT601P can be used for compression or calendering molding of O-rings and gaskets, and extrusion of articles. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 60 | MU | |
| Fluorine Content | 68 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.85 | N·m | |
| ML 2(177°C) | 0.520 | N·m | |
| t'90 3(177°C) | 2.7 | min | |
| ts2 4(177°C) | 2.7 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 14.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 220 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 22 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G30 HUV NTL0001 PC308 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| SLOVAMID® 6 GF 40 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Karina BEIGE PVC COMP. -E 856-08/435-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| Sylvin 83028-90 Green 3195 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 86034-85C Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |