HIFOR® LF1030AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | HIFOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zdfENh_HIFORLF1030AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake LF1030AA is a butene LLDPE designed to enhance extrusion performance, puncture strength, cling force, and ultimate elongation in high-performance cast, coextruded stretch film formulations. Application/Uses
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 19 | µm | |
| secant modulus | ASTM D882 | ||
| 1% sectioning, MD : 19 µm, blown film | 138 | MPa | ASTM D882 |
| 1% sectioning, TD : 19 µm, blown film | 131 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : fracture, 19 µm, blow film | 33.4 | MPa | ASTM D882 |
| TD : fracture, 19 µm, blow film | 15.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : fracture, 19 µm, blow film | 700 | % | ASTM D882 |
| TD : fracture, 19 µm, blow film | 900 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD, Blown Film : 19.1 µm | 23.2 | kN/m | ASTM D1922 |
| TD, Blown Film : 19.1 µm | 104.2 | kN/m | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 19.1 µm, blown film) | 99 | ASTM D2457 | |
| Haze (19.1 µm, blown film) | 1.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for cast film: nominal thickness 0.75 mils; 18 lbs/die inch @ 550° F melt temperature and 80° F chill roll temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 271 - 299 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bluestar Epoxy WSR601 | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| Daelim Po1y® PA-124VS | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Hifax EYS 145P Black | LyondellBasell Industries | PP Copolymer | Hifax |
| Omnix® FC-4050 | Solvay Specialty Polymers | HPPA | Omnix® |
| THERMOLAST® K TC5HFZ (Series: UV/HF/SF) | KRAIBURG TPE | TPE | THERMOLAST® K |