Sarlink® TPE ML-1130N NAT (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zcPtV1_SarlinkTPEML1130NNATPRELIMINARYDATA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink ML-1100 is a general purpose thermoplastic elastomer series, available in NAT and BLK, designed for automotive interior applications. Sarlink ML-1130N NAT is a low hardness, high density, filled grade with good toughness and suitable for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 32 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 30 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 28 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 0.550 | MPa | ISO 37 |
| Flow : 100% strain | 1.01 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 3.30 | MPa | ISO 37 |
| Flow : Fracture | 2.10 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 860 | % | ISO 37 |
| Flow : Fracture | 470 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 12 | kN/m | ISO 34-1 |
| Flow | 16 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 15 | % | ISO 815 |
| 70°C, 22 hr | 39 | % | ISO 815 |
| 90°C, 70 hr | 71 | % | ISO 815 |
| 125°C, 70 hr | 94 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 70 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 120 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | -1.8 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | -16 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 73 | % | ISO 188 |
| Flow : 125°C, 168 hr | 130 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | -7.3 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | -20 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 23 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 99 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 45 | % | ISO 188 |
| Flow : 125°C, 168 hr | 110 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Shao A, 110°C, 1008 hr | -2.1 | ISO 188 | |
| Shao A, 110°C, 1008 hr 8 | -2.2 | ISO 188 | |
| Shao A, 110°C, 1008 hr 9 | -3.6 | ISO 188 | |
| Shao A, 125°C, 168 hr 10 | -2.9 | ISO 188 | |
| Shao A, 125°C, 168 hr 11 | -3.2 | ISO 188 | |
| Shao A, 125°C, 168 hr 12 | -3.5 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 177 | Pa·s | ASTM D3835 |
| Legal statement |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25 - 66 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 5 sec |
| 9 . | 1 sec |
| 10 . | 15 sec |
| 11 . | 5 sec |
| 12 . | 1 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 4040 G10 BK5110 | BASF Corporation | PBT | Ultradur® |
| Cheng Yu E500 | Cheng Yu Plastic Company Limited | PC+PET | Cheng Yu |
| INEOS PP 222-CC50 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| IROGRAN® A 85 P 5350 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| ISPLEN® PR 230 C1E | REPSOL | PP Random Copolymer | ISPLEN® |