Vyncolit® 51-01 CAFR Datasheet,DAP,Vyncolit N.V.-SHANGHAI SUSHENG

Message
Vyncolit 51-01 CAFR is a diallyl phthalate (DAP) material containing mineral fillers. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. The main features of Vyncolit 51-01 CAFR are: flame retardant/rated flame chemical resistance Flame Retardant Good dimensional stability moisture resistance Typical application areas include: Electrical/electronic applications Wire and cable Aerospace military applications

General Information
Filler / Reinforcement	Mineral filler
Features	Good dimensional stability Moisture resistance Antibacterial property Solvent resistance Impact resistance, high Good electrical performance Good chemical resistance alkali resistance Good wear resistance Fuel resistance Heat resistance, high acid resistance Flame retardancy
Uses	Membrane key switch Aircraft applications Insulating material Connector Communication Equipment
Agency Ratings	MIL C-24308
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.75	g/cm³	ASTM D792
Bulk Factor	2.3		ASTM D1895
Molding Shrinkage - Flow (Compression Molded)	0.40 - 0.60	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	55.2	MPa	ASTM D638
Flexural Modulus	8270	MPa	ASTM D790
Flexural Strength	89.6	MPa	ASTM D790
Compressive Strength	145	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	21	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	163	°C	ASTM D648
CLTE - Flow	3.4E-5	cm/cm/°C	ASTM D696
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength			ASTM D149
-- ¹	16	kV/mm	ASTM D149
-- ²	15	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
1 kHz	4.50		ASTM D150
1 MHz	4.30		ASTM D150
Dissipation Factor			ASTM D150
1 kHz	0.020		ASTM D150
1 MHz	0.025		ASTM D150
Arc Resistance	135	sec	ASTM D495
Comparative Tracking Index (CTI)	600	V	UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.59 mm	V-0		UL 94
3.18 mm	V-0		UL 94
Oxygen Index	30	%	ASTM D2863

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	76.7	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	110 - 116	°C
Mold Temperature	160 - 182	°C

Injection instructions
Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secResin Isomer, DAP: OrthoWater Absorption, ASTM D570, 48 hrs, 50°C: 0.55%Flammability Ignition, ASTM D229: 95 secFlammability Burn, ASTM D229: 50 secDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 400 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 375 V/milDielectric Constant, ASTM D150, 1000 Hz, wet: 4.5Dielectric Constant, ASTM D150, 1000000 Hz, wet: 4.3Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.02Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.025Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Injection instructions

Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secResin Isomer, DAP: OrthoWater Absorption, ASTM D570, 48 hrs, 50°C: 0.55%Flammability Ignition, ASTM D229: 95 secFlammability Burn, ASTM D229: 50 secDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 400 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 375 V/milDielectric Constant, ASTM D150, 1000 Hz, wet: 4.5Dielectric Constant, ASTM D150, 1000000 Hz, wet: 4.3Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.02Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.025Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	DAP , Diallyl Phthalate
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zcIvxo_Vyncolit-51-01-CAFR.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
MARPOL® LDC 710	Marco Polo International, Inc.	LDPE	MARPOL®
Sipolprene® 35180	SIPOL S.p.A	TPC-ET	Sipolprene®
Arak LLDPE HD5620EA	Shazand (Arak) Petrochemical Corporation	HDPE	Arak LLDPE
Hanwha Total PE Y910A	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	HDPE	Hanwha Total PE
LUBEMID B27 EL20 NATURAL	LUBEN PLAST srl	Nylon 6	LUBEMID