Order Products : sales@su-jiao.com
LG ASA LI941
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zawTvP_LG-ASA-LI941.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ASA LI941 is an acrylonitrile-styrene-acrylate (ASA) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of LG ASA LI941 are:
The typical application areas of LG ASA LI941 are: automotive industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 25 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 75.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 39 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 170 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 104 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 97.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 5 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | UL 746 | |
| 3.00 mm | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | HB | UL 94 | |
| 3.00 mm, ALL | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Nozzle Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 68.6 - 88.3 | MPa | |
| Screw Speed | < 80 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 280 A | RTP Company | Nylon 6 | RTP |
| SLOVAMID® 6 GF 35 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| StarMediflex P 7070-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| Sylvin 8600-85 Orange 584 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9812-65 Red 683 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |