FLEXAREN® 09009
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Innospec Leuna GmbH |
| Trademark: | FLEXAREN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | za5vCm_FLEXAREN-09009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FLEXAREN® 09009 - high quality ethylene vinyl acetate copolymer with 9% content of vinyl acetate. Manufactured by high pressure tubular process FLEXAREN® 09009 is more elastic than LDPE and compatible with a wide range of polymers. It can be processed with the same equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (20°C) | 0.926 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 9.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 94 | ||
| Shore D | 40 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1BA | ||
| Break | 13.0 | MPa | |
| 50% Strain | 5.90 | MPa | |
| Tensile Strain (Break) | > 700 | % | ISO 527-2/1BA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 100 to 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GAPEX® RPP20EB12WH | Ferro Corporation | PP Homopolymer | GAPEX® |
| Halar® 2408DA | Solvay Specialty Polymers | ECTFE | Halar® |
| Lion Idemitsu Composites PPS C-7010SG | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Plasmer 1070B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Polimid A 25 GF TT/1 | Poliblend S.p.a. | Nylon 66 | Polimid A |