SLOVAMID® 66 GF 30 FRA 5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zZ5ti7_SLOVAMID-66-GF-30-FRA-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66 for injection moulding, reinforced with 30% glass fibre and halogen flame retardant. Application in electrical industry: breakers, coilforms, covers, terminals. Slightly decreased flammability, glow wire 960°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.70 | % | |
| Water Content | 0.10 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 175 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 8900 | MPa | ISO 178 |
| Flexural Stress | 255 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 65 | kJ/m² | |
| 23°C | 70 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 255 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Pressure | 50.0 to 90.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Diakon® ST35G7 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Elastollan® 1385 A | BASF Polyurethanes GmbH | TPU, Unspecified | Elastollan® |
| Geon™ Specialty Suspension Atlas S140 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ Specialty Suspension |
| Karina IVORY PVC COMPOUND -E 851-35/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pujie ACM-04 | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |