CERTENE™ LDF-0522P
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zWHctg_CERTENE-LDF-0522P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-0522P is a certified Blown Film prime grade designed for heavy-duty packaging and industrial applications requiring excellent mechanical properties, such as heavy-duty shipping sacks, pallet shrink, construction, agriculture and liners. LDF-0522P features excellent processability and films exhibit high toughness, high impact and tear strength, and excellent shrink properties. LDF-0522P contains very high antiblock, no UV stabilizer and no slip. LDF-0522P complies with FDA regulation 21CFR 177.1520 (c ) 2.2 and most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm | 186 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 205 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.0 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 31.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 200 | % | ASTM D882 |
| TD : Fracture, 51 µm | 300 | % | ASTM D882 |
| Dart Drop Impact 1(51 µm) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 140 | g | ASTM D1922 |
| TD : 51 µm | 130 | g | ASTM D1922 |
| Additional Information |
|---|
| Film Specimen: 2.0 mils (51 µm) film, melt temperature 380-430°F (195-220°C), blow-up-ratio 2.0 :1. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2606 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Silopren® LSR 2560 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Nipol® NBR N34J | Zeon Corporation | NBR | Nipol® NBR |
| Karina WHITE PVC COMPOUND 806-10/ 236-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Luranyl® HT 190 | ROMIRA GmbH | PPE+Nylon 66 | Luranyl® |