Badamid® A70 SM-Z3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zTl4gs_Badamid-A70-SM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact-modified injection moulding grade, for components and housing with high low-temperature impact resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Yield, 23°C) | 60.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain 2(Yield, 23°C) | 6.0 | 37 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 3(23°C) | 38 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C) | No Break | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength 6(23°C) | No Break | No Break | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 262 | -- | °C | ISO 3146 |
| Maximum Service Temperature | ||||
| 20000 hrs | 70 | -- | °C | |
| some hours | 180 | -- | °C | IEC 216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 9 | 1.0E+13 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity 10 | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity 11(1 MHz) | 3.30 | 3.60 | IEC 60250 | |
| Dissipation Factor 12(1 MHz) | 0.024 | 0.060 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 13 | HB | -- | ||
| 1.60 mm 14 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 125x13x0.8 mm |
| 14 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1290 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tool-A-Thane UT-25 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| Alcryn® 4660 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| HIPOLEN P® MN 1TS | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| Domamid HT™ 7750R15F4H3 Bk-598 | Technical Polymers, LLC | Nylon 66 | Domamid HT™ |