PAXOTHENE® NA112-27
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | USI Corporation |
| Trademark: | PAXOTHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zPxaIF_PAXOTHENE-NA112-27.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PAXOTHENE NA112-27 (LDPE) possesses low melt index and good toughness especially suitable for films with thickness of 0.020~0.100 mm. The said films are for package of shopping bags, frozen bags, re-closable bags and shrink packaging applications. NA112-27 is formulated with medium slip to give good openability of film. High gloss and low haze characteristics of blown film made from NA112-27 provide attractive appearance to the packaged goods thus more valuable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 8.92 | MPa | |
| TD : Yield | 8.92 | MPa | |
| MD : Break | 18.6 | MPa | |
| TD : Break | 15.1 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 340 | % | |
| TD : Break | 550 | % | |
| Dart Drop Impact 1 | 110 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Peak Melting Temperature | 108 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°) | 100 | ASTM D523 | |
| Haze | 7.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K4650 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Zhongfa ABS GR-30 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | ABS | Zhongfa |
| Badamid® LA70 GF35 | Bada AG | Nylon 66 | Badamid® |
| Perfactory® WIC100G | EnvisionTEC, Inc. | Acrylic, Unspecified | Perfactory® |
| Sumiliteresin® PR-51904 | SBHPP | Phenolic | Sumiliteresin® |