Starex LX-0915G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zPKAmz_StarexLX0915G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex LX-0915G is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical appliances. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 17 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.10 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.10 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.10 | % | ISO 2577 |
| Traffic : 3.20mm | 0.10 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 112 | ASTM D785 | |
| R scale | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5620 | MPa | ASTM D638 |
| -- | 6000 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 65.7 | MPa | ASTM D638 |
| Yield | 79.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 73.5 | MPa | ASTM D638 |
| Fracture | 718 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 30 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 4710 | MPa | ASTM D790 |
| -- 6 | 4810 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 93.2 | MPa | ASTM D790 |
| -- 8 | 103 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 54 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 54 | J/m | ASTM D256 |
| 23°C 10 | 6.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 100 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 100 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 97.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 to 3.0mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 71 GF 10 | Plastcom | PP, Unspecified | SLOVALEN® |
| Wellamid® GFT15N050-WBK | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| WELLAMID Nylon 6000 MF 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Arnite® TV4 640 | DSM Engineering Plastics | PC+PBT | Arnite® |
| ELIX™ ABS H607AS | ELIX Polymers, S. L. | ABS | ELIX™ ABS |