Starpylen MK001AS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zOCLG1_Starpylen-MK001AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen MFK001AS is a Mineral Filled Polypropylene Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 2.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.2 | % | |
| Break | 34 | % | |
| Flexural Modulus 1 | 1700 | MPa | ISO 178 |
| Flexural Stress | 41.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 70 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 108 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 44.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.4E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.5E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 215 to 225 | °C | |
| Front Temperature | 225 to 250 | °C | |
| Processing (Melt) Temp | 225 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM 5502BZ | Chevron Phillips Chemical Company LLC | HDPE, HMW | Marlex® |
| POLYLAC® PA-747S | CHI MEI CORPORATION | ABS | POLYLAC® |
| New-prene™ 7050N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Generic LCP | Generic | LCP | Generic |
| Electrafil® ABS C-5 BK MD | Techmer Engineered Solutions | ABS | Electrafil® |