BCC Resins BC 8870
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zO6Xp0_BCC-Resins-BC-8870.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC8870 is a low viscosity two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance. It is recommended for use for the production casting of highly wear-resistant parts and linings. This product is a safe, easy-to-handle, room temperature mixing and curing system that does not contain TDI, MDI, or MOCA. BC8870 is relatively insensitive to typical environmental moisture and will make good void-free parts without the problems that some conventional urethane systems exhibit. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Specific Volume | 0.910 | cm³/g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Life (24°C) | 18.0 to 20.0 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.25 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 to 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 248 | MPa | ASTM D638 |
| Flexural Modulus | 538 | MPa | ASTM D790 |
| Flexural Strength | 25.5 | MPa | ASTM D790 |
| Compressive Strength 1 | 67.6 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | 114 | kN/m | ASTM D624 |
| Compression Set | 72 | % | ASTM D395B |
| Bayshore Resilience | 48 | % | ASTM D575 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 60 | ||
| Thermoset Mix Viscosity | 1800 to 2000 | cP | ASTM D2393 |
| Demold Time (24°C) | 120 to 180 | min | |
| Post Cure Time | |||
| 23°C | 72 to 120 | hr | |
| 66°C | 4.0 to 6.0 | hr |
| Note Message | |
|---|---|
| 1 . | at failure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PC 42 B 35 | SILON s.ro | PP Copolymer | TABOREN |
| Sylvin 8815-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Texin® RxT50D | Covestro - PUR | TPU-Polyether | Texin® |
| Bayblend® T90 XG | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Karina BEIGE PVC COMPOUND 550-08/16-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |