Latimass 53/11-02 D030
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latimass |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zLCeV6_Latimass-53-11-02-D030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.80 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.5 to 1.8 | % | |
| Flow : 2.00 mm | 1.5 to 1.8 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 8.00 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 55.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 40.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 50.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AVP™ GYYHSUVCP | SABIC Innovative Plastics | Nylon 66 | AVP™ |
| Hyundai EP PPF HM980 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| LNP™ LUBRICOMP™ ICL34 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ 2C003 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |
| Lustran庐 ABS 633 | Styrolution | ABS | Lustran® ABS |