Toraycon® 1494X02
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toraycon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zKhSEY_Toraycon-1494X02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toraycon® 1494X02 is a Polybutylene Terephthalate (PBT) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 2.0 | % | |
| Flow : 3.00 mm 2 | 1.5 | % | |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 82 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 64.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 105 | MPa | ISO 178 |
| Coefficient of Friction 3 | 0.18 | ||
| Coefficient of Friction - vs. Metal 4 | 0.140 | Suzuki Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 5(250°C, 1.00 mm) | 9.70 | cm | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 66 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 136 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 64.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant 6 | IEC 60250 | ||
| 23°C, 50 Hz | 3.40 | ||
| 23°C, 1 kHz | 3.40 | ||
| Dissipation Factor 7 | IEC 60250 | ||
| 23°C, 50 Hz | 1.0E-3 | ||
| 23°C, 1 MHz | 0.020 | ||
| Arc Resistance 8 | 70.0 | sec | IEC 60950 |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.397 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | vs. Metal |
| 4 . | Without Lubrication |
| 5 . | 93 MPa |
| 6 . | 60% RH |
| 7 . | 60% RH |
| 8 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P grey homopolymer | Röchling Engineering Plastics SE & Co. KG | PP Homopolymer | POLYSTONE® |
| CERTENE™ PRM-35ARN | Muehlstein | PP Random Copolymer | CERTENE™ |
| Ebalta AH 100 / SR | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| HIVOREX 6010BP | Lotte Chemical Corporation | HDPE | HIVOREX |
| Wanthane® WHT-1172IC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |