LNP™ VERTON™ MVL36SX0 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zHoamg_LNP-VERTON-MVL36SX0-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON MVL36SX0 is a compound based on PP resin containing Long Glass Fiber and PTFE. Added features include: Chemically coupled, Heat Stabilized, Internally Lubricated. Also known as: LNP* VERTON* Compound MFXL-8036 HS BLACK Product reorder name: MVL36SX0 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.73 | % | |
| Flow : 24 hr | 0.37 | % | |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 116 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6500 | MPa | ISO 178 |
| Flexural Stress | 133 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 42 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 5.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 163 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 157 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 199 to 210 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 216 to 221 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® T70 GF30 | Bada AG | Nylon 6/6T | Badamid® |
| Chemraz 655 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Pinnacle PP 4208 | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |
| Polygen SG6C-BK | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| POCAN® B 3235 000000 | LANXESS GmbH | PBT | POCAN® |