AKROLOY® PA GF 50 grey (3807)
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zGgR5r_AKROLOY-PA-GF-50-grey-3807-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced polyamide blend with very high stiffness and strength Applications are components with high dimensional stability, independent from moisture content. AKROLOY PA GF 50 is an alternative for aluminium- and zinc diecast alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.59 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17200 | 16500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 250 | 220 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.7 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 360 | -- | MPa | ISO 178 |
| Flexural Strain at Break 3 | 3.5 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 16 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | |
| 23°C | 110 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 221 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 255 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rigidex® HD6070EA | INEOS Olefins & Polymers Europe | HDPE | Rigidex® |
| Synres-Almoco DAIP 6551 | Synres-Almoco BV | DAP | Synres-Almoco |
| Monprene® OM-10268 | Teknor Apex Company | TPE | Monprene® |
| Generic Nylon 11 - Glass Fiber | Generic | Nylon 11 | Generic |
| LEXAN™ OQ1028 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |