GLAMIDE® T-779
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zFZ3PM_GLAMIDE-T-779.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE®T-779 is a polyamide 6 (nylon 6) product, which contains a 37% mineral filler. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.43 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 10 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.30 - 0.50 | -- | % | ASTM D955 |
| 3.00 mm | 0.80 - 1.3 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 80.0 | 75.0 | MPa | ASTM D638 |
| Yield, 23°C | 65.0 | 35.0 | MPa | ASTM D638 |
| Yield, 80°C | 31.0 | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 16 | 35 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 5900 | 5100 | MPa | ASTM D790 |
| 23°C | 4000 | 1500 | MPa | ASTM D790 |
| 80°C | 1100 | 700 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 140 | 132 | MPa | ASTM D790 |
| Yield, 23°C | 110 | 62.0 | MPa | ASTM D790 |
| Yield, 80°C | 48.0 | 32.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 60 | 82 | J/m | ASTM D256 |
| 23°C | 110 J/m | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 183 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 96.0 | -- | °C | ASTM D648 |
| CLTE - Flow | 7.4E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 21 | 16 | kV/mm | ASTM D149 |
| Arc Resistance | 130 | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 70.0 - 110 | °C | |
| Injection Pressure | 50.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics DC-151 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Axiall PVC 59770 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| DynaPath™ C2050CF | Polymer Dynamix | Nylon 66 | DynaPath™ |
| GERMAMID 6 GF 15 | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| LNP™ LUBRICOMP™ PFN16 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |