Hostacom HBG 479R BLACK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zFWqBo_HostacomHBG479RBLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom HBG 479R BLACK is a 30% glass fiber reinforced PP homopolymer, with low flowability, very good LTHS (long term heat stability) and high rigidity. During the production process an enlarged testing plan is used because of the customer application "pedal support". Please contact Basell for shrinkage recommendations. The product is available in black color, pellet form. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.8 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 4.00 | cm³/10min | ISO 1133 |
| 230°C/5.0 kg | 16.5 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 7000 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| -20°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 52 | kJ/m² | ISO 179/1eU |
| 23°C | 54 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 GB 20 | RTP Company | PESU | RTP |
| Teslin® SP 1800 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| TRIMID® N66-T100 | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Geon™ Vinyl Rigid Extrusion 87759 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Petro Rabigh PP FY2011E | Rabigh Refining & Petrochemical Co. | PP Homopolymer | Petro Rabigh PP |