LUVOTECH®1850-9218 is a polybutene terephthalate (PBT) material, which contains mineral fillers. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOTECH®The main features of 1850-9218 are: anti-warping Good stiffness Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Mineral filler
Features	Low warpage Rigid, good Good strength
Uses	Gear Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.84	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)	21	g/10 min	ISO 1133
Molding Shrinkage	0.20 - 0.50	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	10000	MPa	ISO 527-2
Tensile Stress (Break)	61.0	MPa	ISO 527-2
Tensile Strain (Yield)	1.3	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	14	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	130	°C	UL 746B
Maximum operating temperature- Short Term	180	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+10	ohms	IEC 60167
Surface Resistivity	> 1.0E+10	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	120	°C
Vacuum dryer, B	80	°C
Drying Time
Hot air dryer, A	4.0 - 6.0	hr
Vacuum dryer, B	6.0 - 8.0	hr
Rear Temperature	240 - 260	°C
Middle Temperature	260 - 280	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 265	°C
Processing (Melt) Temp	250	°C
Mold Temperature	60 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	LEHVOSS Group
Trademark:	LUVOTECH®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zF09lT_LUVOTECH18509218.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
DOW™ LLDPE DNDA-1082 NT 7	The Dow Chemical Company	LLDPE	DOW™ LLDPE
DIALAC® S411A	UMG ABS, Ltd.	ASA	DIALAC®
HiFill® PVDF CF30 BK	Techmer Engineered Solutions	PVDF	HiFill®
Lionpol TP-9055ACL	Lion Polymers Incorporated	TPE	Lionpol
Sylvin 8999-70 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin