Order Products : sales@su-jiao.com
LONGLITE® LCP LCP-270 N3G
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zEPIif_LONGLITE-LCP-LCP-270-N3G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LCP-300/ LCP-270 is a high heat-resistance and anisotropic, Type I/ Type II grade Liquid Crystalline Polymer Compound LCP-300/LCP-270 appears low viscosity and high fluidity while operating temperature is higher than its melting point. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 15000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 270 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (2.00 mm) | > 13 | kV/mm | ASTM D149 |
| Arc Resistance | 150 | sec | ASTM D495 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 300 to 320 | °C | |
| Middle Temperature | 320 to 340 | °C | |
| Front Temperature | 340 to 360 | °C | |
| Nozzle Temperature | 340 to 360 | °C | |
| Mold Temperature | 40.0 to 120 | °C | |
| Injection Pressure | 98.1 to 137 | MPa | |
| Holding Pressure | 29.4 to 68.6 | MPa | |
| Back Pressure | 0.800 to 1.00 | MPa | |
| Screw Speed | 40 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 380.5 FR | RTP Company | PC | RTP |
| Witcom PP 2012/078 Blue | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Lucofin® 7440 HFFR | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| TECHNYL® A 60G1 V30 BLACK 15 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Plexar® PX3940X01 | LyondellBasell Industries | PE, Unspecified | Plexar® |