| CAPRAN® 1200M is a 0.47 mil (12 micron) biaxially oriented nylon 6 film with a polymeric coating which provides enhanced adhesion to a variety of inks, coatings, and adhesives. Metallization adhesion is excellent when using "M" coated products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.23 | ASTM D1894 | |
| With self-dynamics | 0.75 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 12 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 12 µm | 2760 | MPa | ASTM D882 |
| TD : 12 µm | 2760 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 12 µm | 255 | MPa | ASTM D882 |
| TD : Break, 12 µm | 255 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 75 | % | ASTM D882 |
| TD : Break, 12 µm | 75 | % | ASTM D882 |
| Oxygen Permeability (25°C, 12 µm) | 1.6 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (12 µm, 38°C, 100% RH) | 380 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 11.9 µm) | 160 - 180 | ASTM D2457 | |
| Haze (11.9 µm) | 2.0 - 3.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield: 51000 in²/lbTensile Strength @ Break, ASTM D 882, MD & TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD & TD: 65 to 90%Secant Modulus, ASTM D 882, MD & TD: 350000 to 450000 psiGraves Tear (initial), ASTM D1004, MD & TD: 1100 to 1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicOxygen Permeability, ASTM D 3985: 3.5 to 4.5 cc/100 in²/dayWater Vapor Transmission, ASTM F 1249: 23 to 26 g/100 in²/daySurface Tension, ASTM 2578, minimum, treated side: >/= 56 dynes/cmSurface Tension, ASTM 2578, Minimum, untreated side: >/= 50 dynes/cmDimensional Stability, ASTM D1204, 320°F, 5 mins, MD: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, 320°F, 5 mins, TD: 0.2 to 0.7% shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraypef® 20030 AP61 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Adstif HA5029 | PolyMirae | PP, High Crystal | Adstif |
| Generic PEBA-Ether | Generic | PEBA-Ether | Generic |
| EL-Pro™ P642J | SCG Chemicals Co., Ltd. | PP Impact Copolymer | EL-Pro™ |
| HiFill® PA6/6 GF43 LE BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |