POLYFORT® FPP 22 T K1093
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z93U3t_POLYFORT-FPP-22-T-K1093.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 22% talc filled PP-Homopolymer with long term heat stabilization |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 80.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2650 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 15 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A50 |
| -- | 86.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 725 | °C | IEC 60695-2-12 |
| 3.00 mm | 725 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 750 | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ESENTTIA 40H92N | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| K-vinyl 105 Deg C Rating Insulation (90-Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| OpteSTAT™ BP 1100 | Ovation Polymers Inc. | TP, Unspecified | OpteSTAT™ |
| PENTAMID AB L5 H1 schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| PENTAMID B GV25 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |