Megalon® 108ST
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mega Polymers |
| Trademark: | Megalon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z5sP3A_Megalon-108ST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified, Type-66 nylon for injection molding applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.5 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.2 | % | |
| Saturation | 6.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, -40°C | 80.0 | MPa | |
| Yield, 23°C | 51.7 | MPa | |
| Yield, 77°C | 40.7 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, -40°C | 20 | % | |
| Yield, 23°C | 40 | % | |
| Yield, 77°C | 220 | % | |
| Flexural Modulus | ASTM D790 | ||
| -40°C | 2760 | MPa | |
| 23°C | 1760 | MPa | |
| 77°C | 483 | MPa | |
| Flexural Strength (23°C) | 67.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 160 | J/m | |
| 23°C | 800 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 216 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 71.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 250 to 260 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 6.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 288 to 310 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen Z11G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| KOPLA PA66 KDG1050 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| INELEC PEEKCF10HF | Infinity LTL Engineered Compounds | PEEK | INELEC |
| Politen® ESP185 | ITEN INDUSTRIES | Polyester Alloy | Politen® |
| KOPHOS® KO1360S | Kolon Plastics, Inc. | PC | KOPHOS® |