SD POLYCA™ PCX-3655
| Category: | PC Alloy , Polycarbonate Alloy |
| Manufacturer: | Sumika Styron Polycarbonate Limited |
| Trademark: | SD POLYCA™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z5MPPC_SDPOLYCAPCX3655.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PCX-3655 is a high heat resistant phosphate type FR PC alloy. This product satisfies V-0 at 1.5mm thickness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2640 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 59.0 | MPa | ASTM D638 |
| -- | 60.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 80 | % | ASTM D638 |
| Fracture | 90 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2350 | MPa | ASTM D790 |
| -- | 2340 | MPa | ISO 178 |
| Flexural Strength | 85.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 59 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 118 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 106 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 2.0 mm | V-0 5VB | UL 94 | |
| 3.0 mm | V-0 5VB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® PG1050A | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Topolymer® 4002 | Dongguan Top Polymer Enterprise | TPEE | Topolymer® |
| Hax™ HF 018/25 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| KOPA® KN133HB30HIBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |