Kepital® FB2030
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z3ArgL_Kepital-FB2030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| An easy-flowing grade for general injection molding. It was reinforced glass beads, and so suitable for parts requiring low warpage and sinking phenomenon. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.63 | g/cm³ | ASTM D792 |
| -- | 1.64 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 18 | g/10 min | ASTM D1238 |
| -- | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | |||
| 2.00 mm | 1.5 | % | ASTM D955 |
| -- | 1.5 | % | |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 57.0 | MPa | ASTM D638 |
| Break, 23°C | 58.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4040 | MPa | ASTM D790 |
| 23°C | 4050 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 97.0 | MPa | ISO 178 |
| Yield, 23°C | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648 |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Electric Strength | 20 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SAP-1607XC60 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |
| Tenac™ GN705 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| SIVIC® 3200 | SIDIAC | NBR | SIVIC® |
| Dryflex® AM 75A202B | ELASTO | SEBS+SBS | Dryflex® |
| LUVOCOM® 1105/GF/40/BK-1 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |