CYCOLAC™ BDT5510 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z0CGlg_CYCOLAC-BDT5510-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Automotive. High heat resistance, low gloss, color concentratable for interior applications. Natural only. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 6.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 14 | g/10 min | ISO 1133 |
| Spiral Flow | 73.7 | cm | Internal Method |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2280 | MPa | ASTM D638 |
| -- | 2930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 2460 | MPa | ASTM D790 |
| -- 4 | 2030 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 67.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 5 | 81.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 179/1eA | ||
| -30°C | 7.2 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 290 | J/m | ASTM D256 |
| -30°C 7 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 8 | 13 | kJ/m² | ISO 180/1A |
| Gardner Impact (23°C) | 35.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 92.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 81.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 83.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| CLTE - Flow (-40 to 60°C) | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 25 | ASTM D523 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1000 sec^-1) | 163 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 193 to 238 | °C | |
| Middle Temperature | 210 to 249 | °C | |
| Front Temperature | 221 to 254 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| New-prene™ 8680N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Nymax™ GF1200 A30 FR BK116 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Boda BDF-KK2801 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| EMOPLEN® AR 1003 RT2 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| EPT 4045 | Mitsui Chemicals, Inc. | EPDM | EPT |