BJB Epoxy TC-1618 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yzkrTz_BJB-Epoxy-TC-1618-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-1618 A/B is an aluminum filled hi-temp epoxy surface coat that provides a tough 90 Shore D surface. This resin compound can be applied with a brush, to a thickness of 1/16" on vertical surfaces or over sharp corners without sag or run-off. TC-1618 A/B features excellent heat resistance with ability to handle constant use at temperatures up to 300°F (149°C). This system does not contain "MDA" or "VCHD". |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.736 | g/cm³ | |
| Part B | 0.978 | g/cm³ |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time (24°C) | 12.0 to 20.0 | hr | |
| Gel Time | 1.0 | hr | |
| Work Time (25°C) 1 | 45.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Mixed : 25°C | 54.0 | Pa·s | |
| Part A : 25°C | 155 | Pa·s | |
| Part B : 25°C | 0.150 | Pa·s |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 88 to 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3720 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 49.6 | MPa | ASTM D638 |
| Flexural Modulus | 5100 | MPa | ASTM D790 |
| Flexural Strength | 97.2 | MPa | ASTM D790 |
| Compressive Strength | 193 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 118 | °C | ASTM D648 |
| CLTE - Flow | 4.2E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 10, Mix Ratio by Volume: 18 | ||
| Shelf Life | 48 | wk |
| Note Message | |
|---|---|
| 1 . | 1 lb mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vistalon™ 8800 | ExxonMobil Chemical | EPDM | Vistalon™ |
| Globalprene® 1485F | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Escorene™ Ultra LD 701.ID | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| LNP™ THERMOCOMP™ RC008H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Hostacom BB 73 F 1648 | LyondellBasell Industries | PP Copolymer | Hostacom |