AvaSpire® AV-848
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yyXdfZ_AvaSpire-AV-848.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AvaSpire® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150°C, including better dimensional stability, lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3100 | MPa | ASTM D638 |
| Tensile Strength 2 | 94.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield 3 | 6.7 | % | ASTM D638 |
| Fracture 4 | 75 | % | ASTM D638 |
| Fracture 5 | 35 | % | ASTM D638 |
| Flexural Modulus | 3300 | MPa | ASTM D790 |
| Flexural Strength | 134 | MPa | ASTM D790 |
| Compressive Strength | 118 | MPa | ASTM D695 |
| Shear Strength | 82.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 252 | °C | ASTM D648 |
| Glass Transition Temperature | 158 | °C | ASTM D3418 |
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| Specific Heat | DSC | ||
| 50°C | 1650 | J/kg/°C | DSC |
| 200°C | 1660 | J/kg/°C | DSC |
| Thermal Conductivity | 0.22 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (0.0500mm, amorphous film) | 180 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.21 | ASTM D150 | |
| 1 kHz | 3.23 | ASTM D150 | |
| 1 MHz | 3.18 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 2.0E-3 | ASTM D150 | |
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 6.0E-3 | ASTM D150 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 6 | 500 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 366 | °C | |
| Middle Temperature | 371 | °C | |
| Front Temperature | 377 | °C | |
| Nozzle Temperature | 382 | °C | |
| Processing (Melt) Temp | 382 - 404 | °C | |
| Mold Temperature | 166 - 193 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Back Pressure: Minimum |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 5.1 mm/min |
| 5 . | 50 mm/min |
| 6 . | @400°C/1000 sec-1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP540-7502(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LEXAN™ 2034 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Karina PVC COMPOUND E 858-10/ 16-ERYA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LTM® 13 | Cytec Industries Inc. | Epoxy | LTM® |
| SCHULARENE™ N3102 | A. Schulman Europe | PLA | SCHULARENE™ |