LNP™ VERTON™ RV00CE compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yxgIlD_LNP-VERTON-RV00CE-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* RV00CE is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. Also known as: LNP* VERTON* Compound RF-700-12 EM Product reorder name: RV00CE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.41 | % | |
| Flow : 24 hr | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 261 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 18900 | MPa | ISO 178 |
| Flexural Stress | 433 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1 | ISO 180/1A | ||
| -40°C | 43 | kJ/m² | |
| 23°C | 54 | kJ/m² | |
| Unnotched Izod Impact Strength 2(23°C) | 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 252 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL6F 802 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| RheTech Thermoplastic Polyolefin FT5100-00 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Nanjing Hongrui PBT T303 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| Hanwha Total TPE SE87 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | TPE | Hanwha Total TPE |
| Innova N 2560 | Innova SA | PS (GPPS) | Innova |