Ultramid® A3EG7 Datasheet,Nylon 66,BASF Corporation-SHANGHAI SUSHENG

Message
Ultramid A3EG7 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profile for aluminium window frames, water containers for automotive cooling systems, as well as electrically insulating parts.

General Information
Filler / Reinforcement	Glass Fiber, 35% Filler by Weight
Features	Good Dimensional Stability High Stiffness Oil Resistant
Uses	Automotive Applications Containers Electrical Parts Housings Machine/Mechanical Parts
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.41	--	g/cm³	ASTM D792, ISO 1183
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)	40.0	--	cm³/10min	ISO 1133
Molding Shrinkage - Flow (3.18 mm)	0.30	--	%
Water Absorption
Saturation	5.0	--	%	ASTM D570
Saturation, 23°C	5.0	--	%	ISO 62
Equilibrium, 50% RH	1.6	--	%	ASTM D570
Equilibrium, 23°C, 50% RH	1.6	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	11500	8500	MPa	ISO 527-2
Tensile Strength
Break, 23°C	207	--	MPa	ASTM D638
Break, 23°C	210	150	MPa	ISO 527-2
Break, 80°C	122	--	MPa	ISO 527-2
Tensile Elongation
Break, 23°C	3.0	--	%	ASTM D638
Break, 23°C	3.0	5.0	%	ISO 527-2
Flexural Modulus
23°C	9860	--	MPa	ASTM D790
23°C	10000	8480	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179
-30°C	12	--	kJ/m²
23°C	14	22	kJ/m²
Charpy Unnotched Impact Strength				ISO 179
-30°C	75	--	kJ/m²
23°C	95	110	kJ/m²
Notched Izod Impact
-40°C	96	--	J/m	ASTM D256
23°C	120	--	J/m	ASTM D256
23°C	14	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	250	--	°C	ASTM D648, ISO 75-2/B
1.8 MPa, Unannealed	250	--	°C	ASTM D648, ISO 75-2/A
Peak Melting Temperature	260	--	°C	ASTM D3418, ISO 3146
CLTE
Flow	1.0E-5	--	cm/cm/°C	ASTM E831
Flow	1.7E-5	--	cm/cm/°C
Transverse	6.5E-5	--	cm/cm/°C
RTI Elec				UL 746
0.750 mm	120	--	°C
1.50 mm	120	--	°C
3.00 mm	120	--	°C
6.00 mm	120	--	°C
RTI Imp				UL 746
1.50 mm	120	--	°C
3.00 mm	120	--	°C
6.00 mm	120	--	°C
RTI Str				UL 746
1.50 mm	130	--	°C
3.00 mm	130	--	°C
6.00 mm	130	--	°C

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity
1.50 mm	1.0E+13	1.0E+10	ohms·cm	ASTM D257
--	1.0E+13	1.0E+10	ohms·cm	IEC 60093
Dielectric Constant (1 MHz)	3.50	5.50		IEC 60250
Dissipation Factor				IEC 60250
100 Hz	0.020	0.30
1 MHz	0.020	0.15
Comparative Tracking Index	550	550	V	IEC 60112

Flammability	Dry	Conditioned	Test Method
Flame Rating			UL 94
1.50 mm	HB	--
3.00 mm	HB	--
6.00 mm	HB	--

Category:	Nylon 66 , Polyamide 66
Manufacturer:	BASF Corporation
Trademark:	Ultramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yw9XZv_Ultramid-A3EG7.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Akulon® K224-G6U	DSM Engineering Plastics	Nylon 6	Akulon®
BESTPOLUX PCX-02	Triesa Plastics	PC	BESTPOLUX
Allen ABS 556/499	SEKISUI Polymer Innovations, LLC	ABS	Allen ABS
EMPOL® BV 307 FR V2	EMAS Plastik San.Tic.AS.	PS (GPPS)	EMPOL®
PENTAMID A E15 H natural	PENTAC Polymer GmbH	Nylon 66	PENTAMID A