ADVANCENE™ EM-4925-AAH
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yuM8fT_ADVANCENEEM4925AAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ EM-4925-AAH HDPE Resin is specifically designed for use in either intermittent or continuous blow molding equipment to produce containers up to 30 liters in size - applications that require the combination of outstanding environmental stress crack resistance (ESCR) and high impact strength. ADVANCENE™ EM-4925-AAH HDPE Resin is also considered a multipurpose blow molding resin designed for the high speed production of blow molded containers used for packaging household industrial chemicals (e.g. detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.) health and medical aids. In addition, it can be blow molded into other thin-walled parts and houseware items, and can also be extruded into profiles or sheets. Main Characteristics
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.949 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/2.16 kg | 0.25 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/21.6 kg | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 180 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 23.4 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 31.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 8.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 900 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 2% Secant | 910 | MPa | ASTM D790B, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | |||
| -- 1 | 210 | kJ/m² | ASTM D1822 |
| -- | 210 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 62.0 | °C | ASTM D648, ISO 75-2/B |
| Brittleness Temperature | < -76.0 | °C | ASTM D746, ISO 974 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 130 | °C | ASTM D3418, ISO 3146 |
| Peak Crystallization Temperature (DSC) | 118 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hanwha Total PP TH74ST | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| KPOL-PP K-PHC 13.0 B | KPOL Chem Co. | PP, Unspecified | KPOL-PP |
| Latilub 80-10T Y/15 | LATI S.p.A. | PPS | Latilub |
| Jampilen HP501M | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| LNP™ THERMOCOMP™ UF0067W compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |