Aclon™ 1090
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | Aclon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ytybmi_Aclon-1090.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclar Flex 180 is a 18-micron (0.70-mil) CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. Its high barrier and excellent dimensional stability make it ideal for flexible packaging applications such as pouches, overwraps, and lidding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.14 | g/cm³ | ISO 1183 |
| Apparent Density | 1.16 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (288°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 42.7 | MPa | ISO 527-2 |
| Fracture | 26.2 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | ISO 527-2 |
| Fracture | 16 | % | ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Flexural Stress | 61.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission Rate (25 µm, 38°C, 100% RH) | 0.25 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 3.2 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 74 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 104 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | °C | ISO 75-2/A |
| Peak Crystallization Temperature (DSC) | 214 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.4 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Bulk Density, ISO 60: 72 lb/ft³Zero Strength, ASTM D1430: 80 to 90 secCrystalline Melting Point, DSC, Tm (initial): 417°FCrystalline Melting Point, DSC, Tm (remelt): 421°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Tuff-X 200 HG | Primex Plastics Corporation | Unspecified | Prime Tuff-X |
| Westlake PVC 1195B | Westlake Chemical Corporation | PVC, Unspecified | Westlake PVC |
| DAI-EL™ G-704 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| FHR Polypropylene AP7810-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| GATONE™ 5630GF | Solvay Specialities India Private Limited (SSIPL) | PEEK | GATONE™ |