LNP™ LUBRICOMP™ DL002ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ytr02x_LNPLUBRICOMPDL002ERcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DL002ER is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release. Also known as: LNP* LUBRICOMP* Compound DL-4020 EM MR Product reorder name: DL002ER |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.79 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.70 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 55.8 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2 |
| Fracture | 49.0 | MPa | ASTM D638 |
| Fracture | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.9 | % | ASTM D638 |
| Yield | 5.8 | % | ISO 527-2 |
| Fracture | 66 | % | ASTM D638 |
| Fracture | 71 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Stress | 73.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.24 | ASTM D3702 Modified | |
| With Self-Static | 0.075 | ASTM D3702 Modified | |
| Wear Factor - Washer | 34.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2500 | J/m | ASTM D4812 |
| 23°C 3 | 170 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 40.2 | J | ASTM D3763 |
| -- | 44.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 125 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 LF Z | RTP Company | PEI | RTP |
| Thermoset Plastics EL-636 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| 4PET® 9L22120 HUV | 4Plas | PET | 4PET® |
| ASTALAC™ ASA 304 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| GERMAMID 6.6 GF 25 V0 | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |