Delrin® FG500TL NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ysa9PQ_Delrin-FG500TL-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Teflon® Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Developed for Food Contact Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.7 | % | |
| Flow | 1.8 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.90 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.17 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 71.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 13 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 20 | % | ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 160 | kJ/m² | |
| 23°C | 170 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 6.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.0E-4 | cm/cm/°C | |
| Transverse | 1.0E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PEI-G30 | Polymer Resources Ltd. | PEI | PRL |
| Vexel 4450 | Custom Resins Group | PBT | Vexel |
| NuSil MED-4942 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| HiFill® POM CO GF10 CC | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Lucet® GC-225 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucet® |