Lucky Enpla LHLD1007
| Category: | PC , Polycarbonate |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yqsUHe_Lucky-Enpla-LHLD1007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LHLD1007 is a polycarbonate (PC) product,. It can be processed by extrusion or injection molding and is available in North America, Europe or Asia Pacific. Lucky Enpla LHLD1007 applications include water pipes/pipes/drinking water and lighting equipment. The main features are: light diffusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 60.8 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2210 | MPa | ASTM D790 |
| Flexural Strength 3 | 90.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 710 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 128 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Nozzle Temperature | 285 - 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 1.96 - 3.92 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 285-310°CInjection Pressure (1st Pressure): 700-1200 kg/cm²Injection Pressure (2nd Pressure): 400-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R228 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Boltaron 1050E | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| Aurora PVC AP1000 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| INSULGEL 50 FC Black | ITW Polymers Coatings North America | Epoxy | INSULGEL |
| LNP™ THERMOCOMP™ DX13354 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |