Plaslube® PA6/6 GF43 ML2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yqP4th_Plaslube-PA6-6-GF43-ML2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plaslube®PA6/6 GF43 ML2 is a polyamide 66 (nylon 66) product, which contains a 43% glass fiber reinforced material. It can be processed by injection molding and is available in North America. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 172 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.31 | ASTM D1894 | |
| With steel-static | 0.24 | ASTM D1894 | |
| Wear Factor | 150 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 263 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 260 | °C | ASTM D648 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 20 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 271 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 79.4 - 104 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: SlowRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 620TIS2 | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| VALOX™ V8030CS resin | SABIC Innovative Plastics | PBT+PET | VALOX™ |
| Bergamid™ A70 G25 U-SO TM | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Cellophane™ 335MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Karina BLACK PVC COMPOUND 771-48/ 1-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |