Diakon® ST15G8
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ypdhw2_Diakon-ST15G8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diakon®ST15G8 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion. Diakon®The main features of ST15G8 are:
Diakon®The typical application field of ST15G8 is: automobile industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.9 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 88 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 77.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 2.1 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | 0.500 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ISO 306/A |
| -- | 105 | °C | ISO 306/B |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542, ISO 489 | |
| Transmittance | 91.5 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Mold Shrinkage, H961/30: .4 to .7% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXTEL® 600T10-BK | MRC Polymers, Inc. | PP, Unspecified | MAXTEL® |
| Novodur® HD M203FC | Styrolution | ABS | Novodur® |
| EPOPLEN PP CFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PP, Unspecified | EPOPLEN |
| Sumiliteresin® PR-7031A | SBHPP | Phenolic | Sumiliteresin® |
| WELLAMID Nylon 6000/42 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |