RTV-2 P-100
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ypQ6HA_RTV-2-P-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
P-100 is a low viscosity, medium tear strength, platinum-catalyzed, RTV-2 silicone rubber, which was designed to have outstanding heat and chemical resistance. It is easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. P-100 may show some inhibition sensitivity. P-100 is extremely useful for casting solid polyurethane, polyurethane foam, polyesters, epoxies and some low melting point metals. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 329 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.802 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 13 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 25000 to 40000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Brown | ||
| -- 3 | Off White | ||
| Viscosity | |||
| -- 4 | 30 to 50 | Pa·s | |
| -- 5 | 1500 to 2500 | Pa·s | |
| Curing Time | 16 to 24 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 6 | 26 to 34 | ||
| Shore A 7 | 26 to 40 | ||
| Tensile Strength | 3.03 to 3.45 | MPa | ASTM D412 |
| Tensile Elongation at Break | 320 to 370 | % | ASTM D412 |
| Tear Strength | 10.5 to 14.0 | kN/m | ASTM D624 |
| Electric Strength | 22 | kV/mm | |
| Relative Permittivity (100 Hz) | 2.10 | ||
| Volume Resistivity | 4.5E+14 | ohms·cm | |
| Dissipation Factor (100 Hz) | 9.0E-3 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Activator |
| 3 . | Base |
| 4 . | Base |
| 5 . | Activator |
| 6 . | 1 Day |
| 7 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 A Z | RTP Company | PC+Acrylic | RTP |
| Monprene® SP-12972 XRD2 | Teknor Apex Company | TPE | Monprene® |
| CYCOLOY™ C7210A resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| Diakon® CLH952LX | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Bergamid™ A700 G15 HW UF NC099 | PolyOne Corporation | Nylon 66 | Bergamid™ |