PLUSTEK PB320G6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yoeUY9_PLUSTEK-PB320G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS-FIBER REINFORCED, FLAME RETARDANT POLYAMIDE 6 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.30 - 0.70 | % | |
| -- | 0.30 - 0.70 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 4.5 | % | ASTM D570 |
| Saturated, 23°C | 4.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9600 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 170 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 90 | J/m | ASTM D256 |
| 23°C | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 215 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | > 200 | °C | |
| Maximum Continuous Use Temperature | 110 | °C | |
| Melting Temperature | |||
| -- | 218 | °C | ISO 11357-3 |
| -- | 220 | °C | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 65 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 4.30 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 230 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Mold Temperature | 55.0 - 95.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS LS | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| TOTAL Polypropylene PPH 12020 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Alathon® M6061 | LyondellBasell Industries | HDPE | Alathon® |
| ASI POLYPROPYLENE 1500-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Karina BLACK PVC COMPOUND 70900-48/1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |