Durethan® BKV 60 EF DUS097 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yoM35W_Durethan-BKV-60-EF-DUS097-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 60 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.60 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.020 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.30 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.030 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 3.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 19400 | 12500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 230 | 158 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 20000 | 13600 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | -- | 250 | MPa | |
| 23°C 6 | 390 | 260 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | 4.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-190, GF60 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.060 to 0.20 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 17 | -- | kJ/m² | |
| 23°C | 17 | 24 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 95 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 18 | -- | kJ/m² | |
| 23°C | 18 | 29 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 95 | 95 | kJ/m² | |
| 23°C | 90 | 90 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 3.80 | -- | J | |
| 23°C | 4.30 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 1350 | -- | N | |
| 23°C | 1480 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 213 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 186 | -- | °C | ISO 75-2/C |
| Melting Temperature 8 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP702A | Southern Polymer, Inc. | HDPE | PRIMALENE |
| RTP 400 UV | RTP Company | PS Alloy | RTP |
| Vital-Line SHE4800 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| ACCUTECH™ HP0339G15M15CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| DIALAC® KVS700 | UMG ABS, Ltd. | AES | DIALAC® |