Lumid® GP1000B(W)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ynqZel_Lumid-GP1000B-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, Low Viscosity Applications Buckles, Chair Nob |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 to 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 80.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 230 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 75.0 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 23 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Arc Resistance | 190 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.700 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 255 to 270 | °C | |
| Middle Temperature | 260 to 275 | °C | |
| Front Temperature | 260 to 275 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure 5 | 0.490 to 1.96 | MPa | |
| Screw Speed | 60 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenogel® ABS A3 HL CR NTLA010 AB325 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| TOTAL Polypropylene PPR 9220 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| ALCUDIA® LDPE CN-102 | REPSOL | LDPE | ALCUDIA® LDPE |
| Flontech® FT-CF15-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| PLUSTEK PA810 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |