Bayblend® FR3012
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ymO0e5_Bayblend-FR3012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; unreinforced; flame retardant; injection molding grade; Vicat/B120 = 102 °C; UL recognition 94 V-1 (1.5 mm); good light stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/5.0 kg) | 26.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 3.5 | % | |
| Break, 23°C | > 40 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.6E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 155 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Toughblend® PA66-1900 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| Wellamid® T-731E-BK | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| POLYCOMPO PE 2100J | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Microthene® MP625962 | LyondellBasell Industries | LLDPE | Microthene® |