THERMORUN® 215B
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | THERMORUN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ykqqIR_THERMORUN-215B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| THERMORUN®215B is a thermoplastic elastomer (TPE) material,. This product is available in North America, Europe or Asia Pacific,. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.4 | % | ISO 294-4 |
| Flow direction | 1.5 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 450 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Yield | 13.0 | MPa | ISO 37 |
| Fracture | 18.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | 800 | % | ISO 37 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-40°C) | 9.0 | kJ/m² | ISO 180 |
| Additional Information |
|---|
| Data obtained using JIS test methods. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PP EC-EM-HI | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| NORYL GTX™ GTX679 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Badaprene® TPV 55A 1049 | Bada AG | PP+EPDM | Badaprene® |
| Elastron® G G100.A90.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina COMP. PVC IVORY -E 600D35/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |