PRL PPX-GP1-(color)-EN
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ykXI0F_PRL-PPX-GP1--color--EN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-GP1-(color)-EN is a polyphenylene ether PS (PPE PS) product,. It can be processed by extrusion and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 4.0 - 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.50 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18mm | 55.2 | MPa | ASTM D638 |
| Fracture, 3.18mm | 48.3 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18mm | 8.0 | % | ASTM D638 |
| Fracture, 3.18mm | 30 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1 |
| Notched Izod Impact | |||
| -40°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 210 | J/m | ASTM D256 |
| -30°C | 4.2 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Dart Drop Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 129 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 121 | °C | ASTM D648 |
| Vicat Softening Temperature | 146 | °C | ASTM D1525 1 |
| RTI Elec (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | °C | UL 746 |
| RTI (1.50 mm) | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 204 | °C | |
| Cylinder Zone 2 Temp. | 227 | °C | |
| Cylinder Zone 3 Temp. | 227 | °C | |
| Melt Temperature | 227 - 254 | °C | |
| Die Temperature | 249 | °C |
| Extrusion instructions |
|---|
| Do not exceed 8 hour drying time. |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Weatherflex™ CS1522WX NTL01B | Colorite Polymers | PVC, Flexible | Weatherflex™ |
| ANSALON A08 000 0000 V0 HF | Daloga srl | PC | ANSALON |
| Daelim Po1y® TR-402 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Karina IVORY PVC COMPOUND -E 655-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/6 CF33 ML2 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |