RTP 1387 TFE 15 SI 2
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yiOCWQ_RTP-1387-TFE-15-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 0.070 | % | ASTM D955 |
| 6.35mm, injection molding | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 34500 | MPa | ASTM D638 |
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 0.50 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 24100 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 227 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, injection molded | 260 | °C | ASTM D648 |
| 1.8 MPa, unannealed, injection molded | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 288 - 321 | °C | |
| Middle Temperature | 288 - 321 | °C | |
| Front Temperature | 288 - 321 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 69.0 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® XRM 5010 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Amilan® CM3004-V0 | Toray Resin Company | Nylon 66 | Amilan® |
| CGPC PVC SO-30X (75 phr Plasticizer D) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Hifax CJ232 | LyondellBasell Industries | TPO (POE) | Hifax |
| LubriOne™ AT-000/20T NC004 ROHS | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |