Next Nylon 6 Prime Series NGM30-01GY
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yhgMf2_Next-Nylon-6-Prime-Series-NGM30-01GY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Glass/Mineral Fiber Reinforced Grey compound Product Applications This grade is commonly used in the Automotive industry to mold a large part with a low warpage Such as Fan blades, engine cover, Heater grill, car body parts, housing. Benefits This grade offers an execellent planarity of the end product, High mechanical property with a high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.37 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.30 | -- | % | |
| Across Flow | 0.85 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.9 | -- | % | |
| Saturation 1 | 6.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 105 | -- | ||
| R-Scale | 115 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 100 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 12 | % | ASTM D638 |
| Flexural Modulus | 6200 | -- | MPa | ASTM D790 |
| Flexural Strength | 140 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | 78 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 205 | -- | °C | |
| 1.8 MPa, Unannealed | 180 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN4720SB01 | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| PRL TP-FR-G15 | Polymer Resources Ltd. | PBT | PRL |
| Ranger PBT PBT-403-M-G15 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Shinko-Lac® ASA FA-40 | Mitsubishi Rayon America Inc. | ASA+PC | Shinko-Lac® |
| Abstron IM11 | Bhansali Engineering Polymers Limited | ABS | Abstron |