| LNP LUBRICOMP JZL012 is a compound based on Polyethersulfone resin containing Proprietary Filler, PTFE. Added features include: Internally Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.80 to 1.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3100 | MPa | ISO 178 |
| Flexural Stress | 106 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 214 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 199 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1690B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| StarFlex P 7130-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | Starflex |
| LNP™ THERMOCOMP™ RX05494 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LubriOne™ AT-000/18T 2S | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| PENTAMID A GK30 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |