Epocast 54 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yhKmrC_Epocast-54-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 54-A/B epoxy laminating system is an unfilled, solvent-free, easy-to-handle product. It is self extinguishing and well suited for the manufacture and repair of composite structures. In addition to laminating applications, the epoxy system can be used for filament winding. Epocast® 54-A/B epoxy laminating system is qualified to AIMS 04-27-000-01. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D792 | ||
| -- 1 | 1.05 | g/cm³ | ASTM D792 |
| -- 2 | 1.19 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus 3 | 23400 | MPa | ASTM D695 |
| Compressive Strength 4(25°C) | 338 | MPa | ASTM D695 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability 5 | FAR 25.853(a) | ||
| Burn Length | 8.89 | cm | FAR 25.853(a) |
| Drip Extinguish Time | 0.0 | hr | FAR 25.853(a) |
| Self Extinguish Time | 0.0 | hr | FAR 25.853(a) |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 100 gms (25°C) | 15.0 - 25.0 | min | ASTM D2471 |
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 15 | ||
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C 6 | 8000 | cP | ASTM D2196 |
| 25°C 7 | 400 | cP | ASTM D2196 |
| 25°C 8 | 9000 | cP | ASTM D2196 |
| Additional Information |
|---|
| CURE SCHEDULE: Five days at 77°F (25°C) or two hours at 150-200°F (66-93°C) after room temperature gel. The system can be handled and machined after 24 hours at room temperature. |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | 12-ply 7781 glass cloth |
| 4 . | 12-ply 7781 glass cloth |
| 5 . | 2-ply 7781 glass cloth, 60 sec., vertical |
| 6 . | System |
| 7 . | Hardener |
| 8 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STERLENE™ RP0100230U | R&P (Pte.) Ltd. | PP, Unspecified | STERLENE™ |
| TAROMID B 280 G6 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Zythane® 6045D | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| Globalene® 73F4-3 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| Sylvin 9451-85UV Black | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |