Clearflex® H&T CLH D0
| Category: | VLDPE , Very Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yhGoAB_ClearflexHampTCLHD0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex CLH D0 is a linear low density polyethylene, with antioxidants, characterised by a very low density (VLDPE). This resin is produced with a proprietary technology. Stretch films manufactured with Clearflex CLH D0 have high stretchability, outstanding clarity and very high constancy in cling effect. Main Applications Clearflex CLHD0 is recommended in all applications where outstanding flexibility and toughness are required. Its peculiar macromolecular structure, as a result of a "unique" proprietary catalyst employed, makes Clearflex CLHD0 the ideal choice for wire and cable compounding and, due to its excellent polyolefin compatibility and fillers acceptance, Clearflex CLHD0 is recommended as impact modifier of PP, with or without mineral fillers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 8 to 50 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% sectioning, MD : 23 µm, cast film | 40.0 | MPa | ISO 527-3 |
| 1% sectioning, TD : 23 µm, cast film | 50.0 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, 23 µm, cast film | 5.00 | MPa | ISO 527-3 |
| TD : yield, 23 µm, cast film | 5.00 | MPa | ISO 527-3 |
| MD : fracture, 23 µm, casting film | 31.0 | MPa | ISO 527-3 |
| TD : fracture, 23 µm, casting film | 26.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : fracture, 23 µm, casting film | 600 | % | ISO 527-3 |
| TD : fracture, 23 µm, casting film | 800 | % | ISO 527-3 |
| Dart Drop Impact (23 µm, Cast Film) | 230 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 23.0 µm | 40.0 | kN/m | ISO 6383-2 |
| TD : 23.0 µm | 82.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 62.0 | °C | ISO 306/A |
| Melting Temperature | 105 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 90 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 1.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 270 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® WR-12058 | Teknor Apex Company | TPE | Monprene® |
| UBE Nylon 1015GU9 | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| CAPROWAX P™ 6006-11-000 Granulat | POLYFEA | Biodeg Polymers | CAPROWAX P™ |
| ExxonMobil™ LDPE EVA Copolymers LD 361 Series | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Mediprene® 880136-02 | ELASTO | SEBS | Mediprene® |